| Powder-Free
Latex Examination Gloves
Overview
Generally used in environments where powder
is not desirable, our non-sterile powder-free
latex examination gloves is the ideal alternative
for those who are hypersensitive to latex protein.
This custom-moulded ambidextrous glove which
comes in a full range of sizes, offers greater
dexterity and a comfortable fit with no finger
fatigue. |
 |
| |
|
|
|
| |
Product Specifications |
|
| |
| Cuff |
: |
Beaded |
| Surface Finishing |
: |
Smooth or Textured |
| Colour |
: |
Glove colour varies from white to yellow, uniform
for each individual piece and allowing for gradual
shift due to thickness variation. |
| Protein Content |
: |
Tested according to ASTM D5712-05
Modified Lowry Method
Maximum : 50 micrograms/dm2 |
| Barrier Defect |
: |
Tested according to ASTM D5151-99
watertight test method
- Inspection level G1
- AQL 1.5 |
| Powder Residue |
: |
Tested according to ASTM 6124-06
Maximum : 2mg per glove |
|
|
| |
|
|
| |
Dimensions
Compliance to ASTM 3578-05 Standard |
|
| |
|
|
| |
|
Size |
Palm Width
(mm) |
Glove
Length
(mm) |
Single-walled
Thickness
(mm) |
| Smooth/
Textured |
Smooth/Textured
|
| Extra
Small |
70
± 10 |
Range
from 230 to 300 as per customer's requirement
|
Cuff:
Min 0.09
Palm: Min 0.11
Finger: Min 0.13 |
| Small
|
80
± 10 |
| Medium
|
95
± 10 |
| Large
|
111
± 10 |
| Extra
Large |
≥ 110 |
|
|
| |
|
|
| |
Physical Properties
Tested according to ASTM D412-98a |
|
| |
|
|
| |
| Test |
Before Aging |
After Aging |
| Tensile Strength |
Minimum 18 MPa |
Minimum 14 MPa |
| Elongation at Break |
Minimum 650% |
Minimum 500% |
|
|
| |
|
|
| |
Tested according to
EN 455 -2 : 2000 |
|
| |
|
|
| |
| Test |
Before Aging |
After Aging |
| Force at Break |
Minimum 9 N |
Minimum 6 N |
|
|